POM 100 美国杜邦100 物性表

供应POM 100 进口原料，免费提供物性表

POM强度高，质轻，常用来代替铜、锌、锡、铅等有色金属， 广泛用于工业机械、汽车、电子电器、日用品、管道及配件、精密仪器和建材等部门。

POM100美国杜邦公司 物性数据

①原料描述部分

规格级别：注塑级外观颜色：乳白色用途概述：用于工种制品备注说明：特性：均聚甲醛，高粘度，具有坚韧的硬度，优良的热稳定性。

　

②原料技术数据

性能项目试验条件[状态]测试方法测试数据数据单位基本性能密度---ASTM D7921.42---吸水量24hrs浸泡+73�H(+23℃)ASTM D5700.25%吸水量Equil.50%R.h.+73�H(+23℃)ASTM D5700.22%吸水量浸泡均衡点+73�H(+23℃)ASTM D5700.90%物理性能绝缘强度Short Time,90 milsASTM D149500V/mil绝缘强度Short Time,2.3mmASTM D14919.7MV/m摩擦系数+73�H(+23℃)静态---0.20ThrustWasherTest3摩擦系数+73�H(+23℃)动态ThrustWasherTest30.35---电阻系数+73°F(+23℃)0.2%H2OASTM D2571015ohm-cm绝缘系数系数 +73�H(+23℃)102to106HzASTM D1503.7---扩散因数+73�H(+23℃)106HzASTM D1500.005---机械性能无切口冲击程度+23℃D256>5300(no break)j/m压缩应力+73°F@10%Def.ASTM D69518.0MPsi压缩应力+23℃@10%Def.ASTM D695124MPa负载下之变形2000psi@+122�H(14Mpa@50℃ASTM D6210.5%弯曲疲劳忍耐限度+73�HASTM D6714.7MPsi弯曲疲劳忍耐限度+23℃ASTM D67132.4MPalzod冲击强度-40�HASTM D2561.8ft.lb/inlzod冲击强度40℃ASTM D25696.1j/mlzod冲击强度+73�HASTM D2562.3ft.lb/inlzod冲击强度+23℃ASTM D256123j/m拉力冲击抵抗力+73�HD1822Long170ft.lb/in²拉力冲击抵抗+23℃D1822Long350KJ/m2无切口冲击程度+73�HASTM D256>100(no break)ft.lb/in断裂时之拉力伸张度-68�H(-55℃)ASTM D63838%断裂时之拉力伸张度+73�H(+23℃)ASTM D63875%断裂时之拉力伸张度+158�H(+70℃)ASTM D638230%断裂时之拉力伸张度+212�H(+100℃)ASTM D638>260%断裂时之拉力伸张度+250�H(+122℃ASTM D638>260%伸张强度-68�HASTM D63814.7MPsi伸张强度-55℃ASTM D638101MPa伸张强度+73�HASTM D63810.0MPsi伸张强度+158�H(+70℃)ASTM D6386.9MPsi伸张强度+70℃ASTM D63847.5MPa伸张强度+212�HASTM D6385.2Mpsi伸张强度+100℃ASTM D63835.9MPa伸张强度+250�HASTM D6383.8MPsi伸张强度+122℃ASTM D63826.2MPa弹性系数+73�HASTM D638450MPsi弹性系数+23℃ASTM D6383100MPa剪力+73�HASTM D7329.5MPsi剪力+23℃ASTM D73265.5MPa挠曲系数-68�H在25℃下530MPsi挠曲系数-55℃在25℃下3650MPa挠曲系数+73�H在25℃下380MPsi挠曲系数+23℃在25℃下2620MPa挠曲系数+158�H在25℃下225MPsi挠曲系数+70℃在25℃下1550MPa挠曲系数+212�H在25℃下130MPsi挠曲系数+100℃在25℃下895MPa挠曲系数+250�H在25℃下90MPsi挠曲系数+122℃在25℃下620MPa弯曲降服强+73�HASTM D79014.3MPsi弯曲降服强+23℃ASTM D79098.6MPa压缩应力缩应力 +73°F@1%Def.ASTM D6955.2MPsi压缩应力+23℃@1%Def.ASTM D69535.9MPa伸张强度+23℃ASTM D-63868.9MPa洛氏硬度---ASTM D785M94,R120---电气性能电弧抵抗力120mil(3.1mm)ASTM D495220no trackingSec.热 性 能热变形温度0.5MpaASTM D648172℃热变形温度1.8MPaASTM D648136℃热变形温度66psiASTM D648342�H热变形温度264psiASTM D648277�H熔点---ASTM D2133347°F熔点---ASTM D2133175℃线性热膨胀系数-40 to +85�HASTM D6965.810-5in/in.�H线性热膨胀系数-40 to +29℃ASTM D69610.410-5m/m.℃线性热膨胀系数+85 to +140�HASTM D6966.810-5in/in.�H线性热膨胀系数+29 to +60℃ASTM D69612.210-5m/m.℃线性热膨胀系数+140 to +220�HASTM D6967.610-5in/in.�H热传导系数------0.37W/mk线性热膨胀系数+60 to +104℃ASTM D69613.710-5m/m.℃线性热膨胀系数+220 to +300�HASTM D6968.310-5in/in.�H线性热膨胀系数+104 to +150℃ASTM D69614.910-5m/m.℃热传导系数------2.6BTU-in/hr其它性能可燃烧性---UL9494HB---